Fatigue et auto-échauffement d'alliages à mémoire de forme en NiTi avec ou sans R-phase

Eduardo Alarcón (1, 2) , Luc Saint-Sulpice (2) , L Heller (1) , Shabnam Arbab-Chirani (2) , Sylvain Calloch (2) , Petr Šittner

1 Institute of Physics [Prague]
2 IRDL - Institut de Recherche Dupuy de Lôme

In this article the structural fatigue performance of superelastic NiTi wires is assessed using hourglass-shaped samples. This non-traditional geometry of NiTi fatigue test samples permits to avoid the random deformation localization processes upon wire deflection, which makes it difficult to interpret correctly S-N and Srain-N curves. Force controlled fatigue tests were performed at different temperatures and were complemented by self-heating measurements. The obtained results aims to shed light on the role of the phase transformations of the material into R-phase and B19' in the cyclic damaging of NiTi wires subjected to repetitive loadings.

Dans cette étude, les performances en fatigue structurelle de fils de NiTi est estimée en utilisant des éprouvettes en diabolo. Cette forme d'éprouvette, non-traditionnelle pour des essais de fatigue du NiTi, permet d'éviter une localisation aléatoire de la déformation au cours de l'allongement qui rend difficile l'étude de la fatigue. Des essais de fatigues pilotés e force ont étés réalisés à différentes températures et ont été complétés par des mesures d'auto-échauffement. Les résultats obtenus permettent de mettre en évidence le rôle des transformations de phase du matériau en R-phase et martensite sur la fatigue des fils de NiTi.

Mots clés: fatigue; auto-échauffement; alliage à mémoire de forme; NiTi; R-phase