Strain rate effects on the thermomechanical behavior of glass/polyester composite joints - ENSTA Bretagne - École nationale supérieure de techniques avancées Bretagne Accéder directement au contenu
Article Dans Une Revue Polymer Composites Année : 2021

Strain rate effects on the thermomechanical behavior of glass/polyester composite joints

Résumé

For several decades, composite materials have been used in different applications due to their multiple advantages. It has become necessary to understand the dynamic behavior of these materials under critical loads. In-plane (IP) and out-of-plane (OP) dynamic compression tests were investigated on a cubic specimen of composite joints under low to high strain rates using the Split Hopkinson Pressure Bars (SHPB) technique. The specimens consist of two adherents (glass/polyester composite) assembled by an adhesive with different thicknesses (1 and 2 mm). During the experimental tests, the high-speed camera was used to check the damage history and the failure mechanisms on adhesively bonded composite joints. The sample surface temperatures were monitored using an infrared camera (IR). For bonding of two composite substrates, it can be noted that the thickness of the adhesive has a significant effect on the dynamic behavior and the kinetics of the damage. It has been concluded that the damage was localized at the level of the layers in the case of in-plane loading and the level of the adhesive zone in the case of out-of-plane loading. The thermomechanical behavior of cubic specimens of adhesively bonded joints subjected to dynamic compression has been studied. The results underline the sensitivity of the dynamic behavior of the adhesively bonded joints to the strain rate, the loading direction and the appearance of heat dissipation linked to the increase in temperature following the initiation of damage. This rise of temperature can dangerously approach the glass transition temperature of the matrix.
Fichier non déposé

Dates et versions

hal-03419567 , version 1 (08-11-2021)

Identifiants

Citer

Mostapha Tarfaoui, Sonia Sassi, Oumnia Lagdani, Mourad Nachtane. Strain rate effects on the thermomechanical behavior of glass/polyester composite joints. Polymer Composites, 2021, 43, pp.36-51. ⟨10.1002/pc.26355⟩. ⟨hal-03419567⟩
47 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More