Transverse Cracking Induced Acoustic Emission in Carbon Fiber-Epoxy Matrix Composite Laminates

Abstract : Transverse cracking induced acoustic emission in carbon fiber/epoxy matrix composite laminates is studied both experimentally and numerically. The influence of the type of sensor, specimen thickness and ply stacking sequence is investigated. The frequency content corresponding to the same damage mechanism differs significantly depending on the sensor and the stacking sequence. However, the frequency centroid does not wholly depend on the ply thickness except for the inner ply crack and a sensor located close enough to the crack. Outer ply cracking exhibits signals with a low-frequency content, not depending much on the ply thickness, contrary to inner ply cracking, for which the frequency content is higher and more dependent on the ply thickness. Frequency peaks and frequency centroids obtained experimentally are well captured by numerical simulations of the transverse cracking induced acoustic emission for different ply thicknesses.
Document type :
Journal articles
Complete list of metadata

https://hal.archives-ouvertes.fr/hal-03512965
Contributor : Aurélien Doitrand Connect in order to contact the contributor
Submitted on : Wednesday, January 5, 2022 - 4:07:29 PM
Last modification on : Tuesday, March 15, 2022 - 3:03:52 AM
Long-term archiving on: : Wednesday, April 6, 2022 - 8:51:28 PM

File

HAMAM2022MATERIALS.pdf
Publisher files allowed on an open archive

Identifiers

Citation

Zeina Hamam, Nathalie Godin, Pascal Reynaud, Claudio Fusco, Nicolas Carrere, et al.. Transverse Cracking Induced Acoustic Emission in Carbon Fiber-Epoxy Matrix Composite Laminates. Materials, MDPI, 2022, ⟨10.3390/ma15010394⟩. ⟨hal-03512965⟩

Share

Metrics

Record views

16

Files downloads

6